Highly Active Nanoperovskite Catalysts for Oxygen Evolution Reaction: Insights into Activity and Stability of Ba 0.5Sr0.5Co 0.8Fe0.2O 2+δ and PrBaCo2O5+δ

Highly Active Nanoperovskite Catalysts for Oxygen Evolution Reaction: Insights into Activity and Stability of Ba 0.5Sr0.5Co 0.8Fe0.2O 2+δ and PrBaCo2O5+δ

TitleHighly Active Nanoperovskite Catalysts for Oxygen Evolution Reaction: Insights into Activity and Stability of Ba 0.5Sr0.5Co 0.8Fe0.2O 2+δ and PrBaCo2O5+δ
Publication TypeJournal Article
Year of Publication2018
AuthorsBae-Jung Kim, Xi Cheng, Daniel F Abbott, Emiliana Fabbri, Francesco Bozza, Thomas Graule, Ivano E Castelli, Luke Wiles, Nemanja Danilovic, Katherine E Ayers, Nicola Marzari, Thomas J Schmidt
JournalAdvanced Functional Materials
Volume28
Issue45
Pagination1804355
Date Published09/2018
Abstract

It is shown that producing PrBaCo2O5+δ and Ba0.5Sr0.5Co0.8Fe0.2O2+δ nanoparticle by a scalable synthesis method leads to high mass activities for the oxygen evolution reaction (OER) with outstanding improvements by 10× and 50×, respectively, compared to those prepared via the state‐of‐the‐art synthesis method. Here, detailed comparisons at both laboratory and industrial scales show that Ba0.5Sr0.5Co0.8Fe0.2O2+δ appears to be the most active and stable perovskite catalyst under alkaline conditions, while PrBaCo2O5+δ reveals thermodynamic instability described by the density‐functional theory based Pourbaix diagrams highlighting cation dissolution under OER conditions. Operando X‐ray absorption spectroscopy is used in parallel to monitor electronic and structural changes of the catalysts during OER. The exceptional BSCF functional stability can be correlated to its thermodynamic meta‐stability under OER conditions as highlighted by Pourbaix diagram analysis. BSCF is able to dynamically self‐reconstruct its surface, leading to formation of Co‐based oxy(hydroxide) layers while retaining its structural stability. Differently, PBCO demonstrates a high initial OER activity while it undergoes a degradation process considering its thermodynamic instability under OER conditions as anticipated by its Pourbaix diagram. Overall, this work demonstrates a synergetic approach of using both experimental and theoretical studies to understand the behavior of perovskite catalysts.